Influences of welding parameters on the quality and creep properties of friction stir welded polyethylene plates

Abstract:

This work aims to investigate the effects of main friction stir welding (FSW) parameters on the quality and creep properties of polyethylene plate joints. Welding variables for analysis were rotational speed, traverse speed, geometry and tilt angle of tool. Indentation creep tests were carried out on weld joints, using a constant load of 1 kgr for 0.5, 2, 5, 15, 30, 60, 90 and 120 min. Also, classical power law, Juhasz, Ashby-Sargent and Mulhearn-Tabor methods were applied for calculating stress exponent values, as a criterion for creep evaluation. The results showed that under special conditions creep resistance of welds are better than that of the base material. Meanwhile, it was found that Mulhearn-Tabor method is the most conservative estimation for assessing the indentation creep behavior of specimens.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

جوشکاری همزنی اصطکاکی آلیاژ برنج و بررسی اثر پارامترهای فرآیند بر روی خواص مکانیکی و سطحی

چکیده:

جوشکاری آلیاژهای برنجی به صورت ذوبی بسیار مشکل است. بزرگترین مشکل جوش ذوبی، تبخیر روی در طی جوشکاری می باشد، همچنین بعد از جوشکاری، قسمت جوش متخلخل خواهد بود. جوشکاری همزنی اصطکاکی که امروزه به عنوان یک روش جدید گسترش یافته است به حل این مشکل کمک می کند. در این جوشکاری هیچگونه ذوبی در ناحیه اتصال دو فلز اتفاق نمی افتد. در تحقیق حاضر، جوش همزنی اصطکاکی بر روی ورق برنج با ضخامت پایین مورد بررسی قرار گرفته است. اثرات سرعت دورانی و سرعت خطی مورد بررسی قرار گرفته اند. پس از انجام جوش، تست های سختی سنجی و کشش بر روی آن انجام گرفته و با مقادیر حاصل از ماده پایه مقایسه شده است. سختی در منطقه جوش نسبت به فلز پایه بهبودی نسبی یافته و استحکام آلیاژ برنج به علت پدیده همزنی در اثر دوران ابزار جوشکاری در ناحیه جوش اندکی کاهش نشان می دهد.

نویسندگان:محمدکاظم بشارتی گیوی، ناصر صادقیان، مرتضی حاجی کرم

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود فیلم جوشکاری ترمیت ریل راه آهن (Railroad thermite welding)

جوشکاری ترمیت (thermite welding) یکی از فرآیندهای جوشکاری است که در آن حرارت مورد نیاز برای ذوب فلز و جوشکاری از طریق یک واکنش شیمیایی به شدت گرمازا تولید می شود. این واکنش بین اجزای یک ترکیب گرمازا مانند مخلوط پودر اکسید فلز و آلومینیوم انجام می گردد. این نوع جوشکاری بیشتر شبیه به ریخته گری بوده و دور دو قطعه ای که باید به هم جوش داده شوند یک قالب شنی یا سرامیکی قرار دارد که فلز مذاب ناشی از این واکنش شیمیایی به این قالب هدایت شده و  پس از سرد شدن فلز مذاب داخل قالب جوش شکل می گیرد. فلز مذابی که در این واکنش تولید می شود پس از انجماد به عنوان فلز پرکننده Filler Metal عمل کرده و قطعات را به هم جوش می دهد.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود پاورپوینت جوشکاری اصطکاکی اغتشاشی (FSW) فولاد زنگ نزن

فایلی که در این بخش خدمت شما عزیزان برای دانلود ارائه کرده ایم پاورپوینتی به زبان انگلیسی با موضوع جوشکاری اصطکاکی اغتشاشی فولاد زنگ نزن (FSW Of Stainless Steel) می باشد. این فایل از 42 اسلاید تشکیل شده و با حجم 4MB از لینک دانلود به راحتی قابل دریافت می باشد.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود استاندارد Ansi/Asnt Cp-105-2011

عنوان استاندارد Ansi/Asnt Cp-105-2011 صلاحیت پرسنل تست های غیر مخرب (Qualification of Nondestructive Testing Personnel) است و برون نمای کلی برای صلاحیت افرادی که تست های غیر مخرب را انجام می دهند، آموزش می دهد. این استاندارد شامل افرادی می شود که برای انجام وظایف و شغل های خود نیاز به دانش فنی مناسب از اصول فنی و اساسی تست های غیر مخرب NDT دارند. این استاندارد در سال 2011 جایگزین استاندارد SNT-TC-1A مربوط به صلاحیت و گواهینامه پرسنل تست های غیر مخرب شده است.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود کتاب Fatigue design of welded joints and components (طراحی خستگی اتصالات و اجزاء جوشکاری شده)

نام لاتین کتاب: Fatigue design of welded joints and components

نام فارسی کتاب: طراحی خستگی اتصالات و اجزاء جوشکاری شده

نویسنده: A.Hobbacher (انستیتو بین المللی جوش IIW)

تعداد صفحات: 130

ناشر: ABINGTON PUBLISHING

سال انتشار: 1996

توضیحات در سایت آمازون:

These recommendations present general methods for the assessment of fatigue damage in welded components, which may affect the limit states of a structure, such as ultimate limit state and serviceability limited state. Fatigue resistance data is given for welded components made of wrought or extruded products of ferritic/pearlitic or banitic structural steels up to fy = 700 Mpa and of aluminium alloys commonly used for welded structures.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود پوستر استانداردهای آزمایش های غیر مخرب در سازمان بین المللی استاندارد ISO

تصویر کوچک این پوستر:

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

Hydrogen interaction and stress-corrosion in hydrocarbon storage vessel and pipeline weldings

Abstract:

This paper addresses important technical problems of H-embrittlement/safety and stress corrosion cracking (SCC) phenomena which can be of concern in various industrial sectors of vessels and pipeline production, including H storage.

Intercrystalline and intergranular cracks have been detected in narrow welded zones having particular hardness, gradually rising from little dimensions till crossing all the plate thickness. Such cracks are due to the residual stresses (RS) produced by the construction technique and to the presence of aggressive elements. H+ diffusion from sulphured hydrogen molecule toward the ferritic material of the internal surface can produce fissures similar to hydrogen-induced cracking (HIC), especially in the presence of RS. Microanalyses have revealed a sulphur deposit formation in the cracks fracture surfaces, as a presence of H2S dragged by LPG fluids. The LPG release due to such cracks in interred vessels near domestic buildings can be dangerous, and an analysis project of its process is under development.

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

بررسی اثر عملیات حرارتی بر ریزساختار شفت توربین بخار لایه نشانی شده توسط فرآیند جوشکاری TIG

چکیده:

شفت های نیروگاهی از نظر جوشکاری دارای مشکلاتی نظیر تشکیل فاز مارتنزیت، آستنیت باقی مانده، حساسیت به ترکیدگی سرد، ایجاد تنش های پسماند و ... می باشند. انتخاب صحیح روش و متغیرهای جوشکاری، تعیین فلز پرکننده و انجام عملیات حرارتی مناسب پس از جوشکاری سبب کاهش چنین مشکلاتی خواهد شد. با توجه به مقدار کربن و عناصر آلیاژی فولاد شفت 5 11 26 NiCrMoV، سیم جوش کم هیدورژن کروم - مولیبدن دار برای جوشکاری لایه نشانی سطح فولاد شفت انتخاب گردید. پس از انجام فرآیند جوشکاری، عملیات حرارتی آنیل و نرماله روی نمونه صورت گرفت و با نمونه ی بدون عملیات حرارتی مقایسه گردید. هدف از انجام این پژوهش تعیین عملیات حرارتی مناسب پس از جوشکاری و بررسی ویژگی های فلز جوش و HAZ با استفاده از آزمون های میکروسختی، XRD ،SEM و میکروسکوپ نوری بود. با توجه به نتایج متالوگرافی مربوط به ریزساختار و XRD نمونه ها، مشاهده شد که در عملیات حرارتی نرماله فازهای کاربیدی بیشتری در زمینه حل شده اند که سبب شده تا تغییرات سختی در منطقه جوش و فلز پایه نسبت به سایر شرایط کمتر باشد. در نتیجه نمونه جوشکاری شده با سیم جوش کروم - مولیبدن دار و تحت عملیات حرارتی نرماله، ساختار و توزیع سختی مطلوب تری داشت.

نویسندگان:اسماعیل گنجه، علی رهبردوست، علی شکوه فر

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.

دانلود فیلم برشکاری زیر آب (Underwater Cutting)

- به دلیل به روز بودن وبلاگ از سایر قسمت ها هم بازدید کنید.

- برای ورود به بخش آرشیو مطالب اینجا را کلیک کنید.