تاثیر انجماد بر تحول ریزساختاری فلز جوش پایه نیکل

Influence of solidification on the microstructural evolution

of nickel base weld metal

تاثیر انجماد بر تحول ریزساختاری فلز جوش پایه نیکل 

ABSTRACT

The effect of segregation resulting from solidification on the microstructural evolution of nickel base alloys was investigated. Two different groups of alloys were produced to simulate either the Hastelloy C type or the Inconel 625/718 type of alloys. Gravitational thermal analysis welding was performed on these experimental alloys and the extent of microsegregation in the weld metal was determined. Using composition profiles obtained from solidified microstructures, predictions of the phase stability of these microstructures were made based on metal d-level (Md) calculations. The maximum Md values obtained in these microstructures were compared with those critical to the formation of topologically close-packed (TCP) phases such as sigma, P, and Laves. These profiles showed an increase in the Md level in the interdendritic regions which was correlated to the formation of TCP phases.

  

 

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

اثر جدایش ناشی از انجماد بر تحول ریزساختاری آلیاژهای پایه نیکل مورد بررسی قرار گرفت. دو گروه مختلف از آلیاژها تولید شدند تا آلیاژهای هاستالوی نوع C یا اینکونل 625/718 را شبیه سازی کنند. جوشکاری آنالیز حرارتی گرانشی بر روی این آلیاژهای آزمایشگاهی انجام شد و میزان میکروجدایش در فلز جوش تعیین شد. با استفاده از پروفایل های ترکیب بدست آمده توسط ریزساختار انجماد یافته، پیش بینی های پایداری فاز این ریزساختارها بر اساس محاسبات تراز d فلز (Md) صورت گرفت. ماکزیمم مقادیر Md بدست آمده در این ریزساختارها با مقادیر بحرانی مربوط به تشکیل فازهای بسیار فشرده توپولوژیکی (TCP) نظیر سیگما، P و Laves مقایسه شدند. این پروفایل ها افزایشی در میزان Md در نواحی دندریتی نشان داد که به تشکیل فازهای TCP مربوط شد.