تحقیق روی رفتار خوردگی اتصالات لحیم کاری مس

Investigation on Corrosion Behaviour of Copper Brazed Joints 

تحقیق روی رفتار خوردگی اتصالات لحیم کاری مس

ABSTRACT

DHP (Deoxidized High Phosphorus(copper is widely used in various heat transfer units such as, air conditioners, refrigerators, evaporators and condensers. Copper sheets and tubes (ISODHP) were brazed with two different brazing alloys. Corrosion resistances of the joints were examined by polarization test. The selected fillers consisted of a silver-based brazing alloys (hard solder); AWS-BCu5, and a copper-based filler AWS BCuP2. All the joints were brazed utilizing two different brazing processes including furnace brazing under argon and air atmosphere. All of the fillers were used with and without flux. The microstructure of the brazed sheets was examined using both optical and scanning electron microscope (SEM). Hardness and leak tests were carried out on all the brazed tubes. In all brazing alloys selective and galvanic corrosion were observed in filler metals, but in copper phosphor alloys the copper adjacent to the joints were noticeably corroded by pitting method. It was found that the samples brazed with BAg5 filler metal using argon furnace show a higher resistance to corrosion. They also have a good ductility in the brazed zone.

 

رفتار خستگی خوردگی آلیاژ آلومینیوم جوشکاری شده

Corrosion fatigue behaviour of aluminium alloy 6061-T651 welded

using fully automatic GMAW and ER5183 filler alloy

رفتار خستگی خوردگی آلیاژ آلومینیوم 6061-T651 جوش داده شده با (GMAW)

با آلیاژ ER5183 به عنوان فیلر

ABSTRACT

The fatigue life of aluminium 6061-T651 at various applied stress amplitudes in the unwelded and welded condition was found to be significantly reduced on immersion in a 3.5% NaCl simulated sea water solution, compared to that measured in ambient air. The ratio of fatigue life in NaCl test solution to that in air increased as the stress amplitude decreased. The observed reduction in the fatigue life in the NaCl test solution was most likely due to the presence of pits which nucleated on second phase particles or precipitates. Welded joints performed using pulsed gas metal arc welding and ER5183 filler wire failed at the interface between the weld metal and the heat-affected zone as a result of a high pitting rate in this region.

  

رفتار خستگی خوردگی آلیاژ آلومینیوم جوشکاری شده

Corrosion fatigue behaviour of aluminium alloy 6061-T651 welded

using fully automatic GMAW and ER5183 filler alloy

رفتار خستگی خوردگی آلیاژ آلومینیوم 6061-T651 جوش داده شده با (GMAW)

با آلیاژ ER5183 به عنوان فیلر

ABSTRACT

The fatigue life of aluminium 6061-T651 at various applied stress amplitudes in the unwelded and welded condition was found to be significantly reduced on immersion in a 3.5% NaCl simulated sea water solution, compared to that measured in ambient air. The ratio of fatigue life in NaCl test solution to that in air increased as the stress amplitude decreased. The observed reduction in the fatigue life in the NaCl test solution was most likely due to the presence of pits which nucleated on second phase particles or precipitates. Welded joints performed using pulsed gas metal arc welding and ER5183 filler wire failed at the interface between the weld metal and the heat-affected zone as a result of a high pitting rate in this region.